Laminating film Each heat sealing material
Composite film composite if the use of water-based glue how to achieve the best composite effect, how good after the compound of the aging process so that the peel strength is better, the following will be one by one description!
1, can be diluted with water?
At present, the water-based glue on the market is mostly emulsion type. The principle is that the macromolecule-dependent emulsifier is stable in water. It is actually a metastable state. Many external forces will cause the glue to break the emulsion and lose effect.
Therefore, it is not recommended to dilute the glue with water. Because dilution with water increases the surface tension of the glue, destroying the stability of the glue, resulting in delamination. In addition, dilution will change the surface properties of the product, resulting in poor wetting, affecting the composite appearance.
2, with water-based adhesive film, the need for aging?
Water-based plastic composite film generally do not need to ripen, the machine can be cut. Appropriate ripening for a period of time, can improve the peel strength, because the high molecular weight of water-based glue, need a certain time to achieve a better level of leveling. Therefore, when the conditions of the composite membrane at 50 ℃ cooked room curing 1h ~ 4h better. The higher temperature (above 80 ℃) aging has a certain effect on the strength of the composite film, because the water-based polymer can not withstand long-term high temperature.
Composite packaging of the heat sealing layer due to the different use of different areas and functional, the use of materials is different, each heat sealing materials which have different characteristics, the following will be your one by one analysis.
First, polyethylene film
Polyethylene for composite heat sealing, mainly low-density polyethylene and linear low-density polyethylene (also some products used in the density and high density polyethylene film to do heat sealing layer), and generally more use of two polyethylene A certain proportion of blending after use. According to the different processing methods, can be divided into blown film, cast film and extrusion coating film. The thickness of the composite polyethylene film, depending on the requirements of the package, choose a different thickness, thin can be about 20μ, thick can be greater than 100μ. Since there are many additives in the resin for the production of films, especially slip agents, attention should be paid to the migration of additives in production.
Previous: Transparency Film 11x17 Office Depot
- Introduction To Laminate
- Application Of Laminate
- Analysis Of Quality Problems
- The Difference Between Laminate And...
- Laminate Countertops Pros And Cons
- Solar Laminate Components/solar Lam...
- Phenolic Cotton Cloth Laminate Defi...
- Multilayer Lamination Parameter Con...
- Laminate Products Can Be Divided In...
- Elaborate In High Temperature Resis...
- A Barbecue Party
- Transparency Film 11x17 Office Depot
- Laminate Film A4
- Transparency Film For Laser Printer...
- Laminating Film Composites
- Matt Laminating Pouches Curing Temp...
- Three-layers Laminating Pouches Pac...
- Lamination Film
- Laminating Pouches 5 Mil Legal
- Charity Sale